use two toolpath as Gerry mentioned..

the first make as climb milling, and leave really just a little on climbmilling don't chips the wood..

at finish pass use the conventional and that little pass wont pull the splinters out..

the reason for this because the first climbing pass will ""bend"" fibers ... as you go against these fibers with the finish that will smooth it out..
otherwise you get fuzzy always, you can find it when you stain or make wet a little the surface..
only way avoid fuzzy if oyu could go as you sharp pencil.. always down on grains.. of course it is not possible in the practical life.. but you can greatly minimize..

another thing is , those diagonal marks shows your bit also was resonating.. that also makes worst..